I personally do all my bevels and grinding after heat treating. There is a reason I do this. I perfer to work with mostly 1095 steel. 1095 is a prone to warpage, I hated having to redo or toss my blades because they would banana on me. Alot of the reason was that at the time I had a charcoal forge and it would heat the blade unevenly.